摘要：本文着重对聚酯型和聚醚型两类水性聚氨酯丙烯酸树脂的固化条件进行研究。首先是根据配方合成水性聚氨酯丙烯酸树脂，在树脂中加入波段不同的光引发剂，干燥后利用光引发剂不同的紫外光波段进行固化，然后通过测试耐水性、耐醇性、耐磨性、硬度等，分析其结构和固化机理，从而确定一个使该树脂在性能方面最优良的固化条件。研究表明无论是聚酯型树脂还是聚醚型树脂，在299～366nm这一波段下固化后，性能最优良。22900
毕业论文关键词：水性聚氨酯树脂；紫外固化；性能；波段；固化条件
Synthesis and Curing of UV curable waterborne polyurethane resin
Abstract: This article focuses on two types of polyester and polyether-type study on curing conditions for waterborne Polyurethane acrylic resin.First based on synthesis of waterborne polyurethane-acrylate resin formulation, and joined bands of different photoinitiators in the resin, after drying using UV wavelengths of photoinitiators different curing, and then tested for water resistance, ethanol resistance, wear resistance, hardness, analysing its structure and reinforcement mechanism to determine a curing of the resin the best in terms of performance. Studies indicate either polyester or polyether resins resin in the band 299 ~ 366nm after curing, the best performance.
Keywords: Waterborne polyurethane resin; UV curing; performance; band; curing conditions
目    录
1前言    1
1.1水性紫外固化聚氨酯丙烯酸酯树脂的概述    1
1.2水性紫外固化聚氨酯丙烯酸酯树脂的特点    2
1.2水性紫外固化聚氨酯丙烯酸酯树脂的固化发展    2
1.3光引发剂907、TPO、2022    3
1.4研究意义及目的    4
2试验    5
2.1原料名称、规格和来源    5
2.2水性紫外固化聚氨酯丙烯酸酯复合树脂的固化装置    5
2.3水性紫外固化聚氨酯丙烯酸酯树脂的构成    6
2.4水性紫外固化聚氨酯丙烯酸酯树脂交联机理    6
2.5水性紫外固化聚氨酯丙烯酸酯树脂基本反应    7
2.6水性紫外固化聚氨酯丙烯酸酯树脂的固化    8
2.7水性紫外固化聚氨酯丙烯酸酯树脂合成制备工艺    8
2.7.1紫外光固化水性聚氨酯丙烯酸树脂的合成    9
2.7.2紫外光固化水性聚氨酯丙烯酸树脂的干燥    9
2.7.3紫外光固化水性聚氨酯丙烯酸树脂的固化成膜    9
2.8水性聚氨酯丙烯酸酯树脂的性能要求    9
2.9水性紫外固化聚氨酯丙烯酸酯树脂的性能测试    10
2.9.1水性树脂固含量的测定    10
2.9.2水性树脂耐水性的测定    11
2.9.3水性树脂耐醇性的测定    11
2.9.4水性树脂吸水率的测定    11
2.9.5水性树脂吸醇率的测定    11
2.9.6水性树脂红外测试    12
2.9.7水性树脂邵氏硬度的测定    12
2.9.8水性树脂耐磨性的测定    12
3结果与讨论    13
3.1水性聚氨酯丙烯酸酯树脂的合成工艺的条件控制说明    13
3.2水性聚氨酯丙烯酸酯树脂乳化分散的工艺条件研究    13
3.3水性聚氨酯丙烯酸酯树脂的结构表征    14
3.4光引发剂用量对水性紫外固化聚氨酯丙烯酸酯树脂胶膜性能的影响    15
3.5固化条件对水性聚氨酯丙烯酸酯树脂吸水率的影响    16 UV固化水性聚氨酯树脂的合成与固化研究:http://www.youerw.com/huaxue/lunwen_15890.html