摘要：以草酸溶液和硝酸铈溶液为原料，在表面活性剂聚乙烯吡咯烷酮（PVP）的帮助下，利用磁力搅拌的方法，合成配位聚合物草酸铈纳米多级结构。对产物进行傅里叶红外光谱（FT-IR）、X-射线衍射（XRD）、扫描电子显微镜（SEM）及热重分析（TGA）表征，研究合成条件如反应时间、PVP量、溶剂对纳米多级结构的影响。结果表明红外光谱实验结果与晶体结构相符，热重分析显示此配位聚合物经过两个分解过程。以草酸铈为前驱体，在空气气氛中煅烧得到CeO2。78195

毕业论文关键词：磁力搅拌，草酸铈，二氧化铈，多级结构,

Abstract: Using magnetic stirring method，nano hierarchical structure coordination polymer of Oxalic acid cerium has been synthesized with oxalic acid solution and cerium nitrate solution as raw material and polyvinylpyrrolidone (PVP) as surface active agent。Cerium(III) oxalate hydrate has been characterized by Fu Liye infrared spectroscopy (FT-IR), powder X- ray diffraction (XRD), scanning electron microscopy (SEM) and thermal analysis (TGA)。Systematic investigations have been performed on the factors influencing the morphology of (C6 H12 Ce2 O18)n,4n(H2 O) nanostructures, such as reaction time, the amount of PVP, the solvent 。 The experimental results show that the infrared spectra are corresponding with the crystal structure and thermogravimetric analysis shows that the coordination polymer occurs three decomposition processes。 By using the Ce(III) oxalate hydrate as precursor, CeO2 has been obtained through calcination in atmosphere。

Keywords: magnetic stirring, Cerium(III) oxalate hydrate, cerium oxide, hierarchical structure 

目  录

1 前言 5

2 实验部分 5

2。1 仪器 5

2。2 试剂 6

2。3 草酸铈的制备 6

2。3二氧化铈的制备 6

3 结果与讨论 6

3。1 草酸铈的XRD分析 6

3。2草酸铈的FT-IR分析 7

3。3 草酸铈的UV分析 8

3。4草酸铈的荧光分析 9

3。5 草酸铈的TGA分析 10

3。6草酸铈的SEM分析 11

3。6。1反应时间对花状草酸铈结构的影响及形成机理 12

3。6。2表面活性剂PVP量对草酸铈结构的影响 13

3。7 草酸铈的BET分析 15

3。8煅烧花状草酸铈制得样品的分析 16

3。8。1煅烧花状草酸铈制得样品的XRD分析 16

3。8。2煅烧花状草酸铈制得样品的SEM分析 17

3。8。3煅烧花状草酸铈制得样品的BET分析 18

结   论 19

参考文献 20

致谢 21

1 前言

二十世纪60年代以来陆续发现稀土化合物具有一系列特殊的药效作用，最早在医药中应用的是铈盐。如草酸铈可用于治疗海洋性晕眩和妊娠呕吐，已载于药典。我国是稀土之邦，矿藏量居世界首位，稀上资源的开发利用在当今经济发展中具有不可估量的作用和特殊的战略地位，对稀土化合物的研究有其特殊意义。 花型微纳米草酸铈的可控合成及结构表征:http://www.youerw.com/huaxue/lunwen_90057.html