摘要本文对铝合金螺柱焊强度不高、性能不太好的问题，以厚度为20mm 的6061铝板，材料为LY12螺柱为主要研究对象，针对16mm和12mm的螺柱进行铝合金螺柱焊工艺的探索性研究，并提出了一种新型螺柱焊的工艺：感应+拉弧复合热源螺柱焊接 。并且在针对铝及铝合金螺柱焊焊接特性的基础上，选用了一种采用钎剂与气体联合保护形式的拉弧螺柱焊接。按照控制变量法展开了螺柱钎焊的工艺试验研究工作，并进行了接头力学性能和微观组织的检测分析，得到了最佳的焊接工艺参数。68190
毕业论文关键词：感应预热，气体保护，钎剂保护，铝合金拉弧螺柱焊
毕业设计说明书（论文）外文摘要
Title High strength aluminum alloy stud induction + drawn arc Hybrid Welding Process Study
Abstract
In this paper, aluminum stud welding strength is not high, the performance is not very good question, with a thickness of 20mm 6061 aluminum, the material is the main object of study LY12 stud for 16mm and 12mm aluminum studs for stud welding process exploratory research, and presents a new stud welding process: induction + arc hybrid welding stud welding. And in the stud welding for aluminum and aluminum alloy welding characteristics, based on the selection of an agent using brazing joint protection in the form of a gas arc stud welding. Carried out according to the control variable method stud brazing process test research work, and conducted joint mechanical properties and microstructure detection analysis, the optimum welding parameters.
Keywords: Induction heating, gas protection, brazing flux protection，aluminum alloy drawn arc stud welding
目 次
1 绪论 1
1.1 课题研究背景及选题意义 1
1.2.1铝合金拉弧螺柱焊 1
1.2.2国内的铝合金螺柱焊接的技术现状 2
1.2.3国外的铝合金螺柱焊接的技术现状 3
1.3 感应加热技术 3
1.3.1 感应加热技术的原理 3
1.3.2 感应加热的性能和特点 3
1.3.3 感应加热设备 4
1.4铝合金螺柱焊的技术难点 4
1.5 本文研究的主要内容 5
2实验材料、设备及方法 5
2.1试验材料 5
2.2试验设备 9
2.3实验方法 14
3感应+拉弧复合热源对铝合金螺柱焊接的工艺研究 15
3.1预热温度对螺柱焊接质量的影响研究 15
3.1.1 试验结果及分析 15
3.2焊接电流对感应+拉弧复合热源铝合金螺柱焊的影响 19
3.2.1 电流对复合热源焊接16mm铝合金螺柱焊的影响 19
3.2.2 电流对复合热源焊接12mm铝合金螺柱焊的影响 22
3.3本章小结 26 高强铝合金螺柱感应+拉弧复合热源焊接工艺试验研究:http://www.youerw.com/cailiao/lunwen_76644.html