摘要研究储氢材料对硝酸酯类炸药的影响。本文通过 SEM 实验、DSC 实验、ARC 实验、 机械感度实验分别研究了 Mg(BHx)y 对硝酸酯类炸药（40%硝化棉+60%硝化甘油）能量性 能、热分解性能、机械感度的影响。研究发现 Mg(BHx)y 会催化硝酸酯类炸药的热分解过 程，但是会降低硝酸酯类炸药的反应焓变；Mg(BHx)y 会提高硝酸酯类炸药的热分解速度， 使其能量更加集中、快速地释放出来。当含有 5%Mg(BHx)y 的硝酸酯类炸药加热至 160℃ 以上是，会在某温度下突然提高分解速率，提高 Mg(BHx)y 的质量分数会降低这一效果。78920

Mg(BHx)y 可以降低硝酸酯类炸药的机械感度，提高其稳定性。
毕业论文关键词 硼氢化镁 硝化棉 硝化甘油 ARC

Title Application of hydrogen storage material in nitrate explosives 

Abstract Influence of hydrogen storage materials on nitrate explosives。Nitrate explosives (40% nitrocellulose + 60% nitroglycerin) were observed by SEM ， DSC, ARC and mechanical sensitivity,respectively on nitrate explosive energy performance and thermal decomposition performance and mechanical sensitivity。Research found that the Mg(BHx)y catalytic nitrate explosive thermal decomposition process, but will reduce nitrate explosive reaction enthalpies; Mg(BHx)y will improve nitrate explosive thermal decomposition rate and the energy more focused, rapid release。 When the nitrate explosive containing 5% Mg(BHx)y nitrate is heated to more than 160℃, it will suddenly increase the decomposition rate at a certain temperature, improve the quality of Mg(BHx)y will reduce the effect。Mg(BHx)y can reduce the mechanical sensitivity of nitrate explosives and improve its stability。

KeywordsMg(BHx)yNitrocelluloseNitroglycerin ARC

目 录

1 绪论 1

1。1 研究的背景及意义 1

1。2 储氢材料的发展概况 1

1。3 储氢材料在含能材料中的应用 2

1。4 学位论文主要研究内容 4

2 含硼氢化镁的硝酸酯炸药的制备 5

2。1 样品的制备方法 5

2。2 样品的 SEM 分析 5

3 差示扫描量热法(DSC)对热分解性能的研究 7

3。1 样品的制备与实验条件 7

3。2 实验结果与分析 7

3。3 本章小结 11

4 绝热加速量热法(ARC)对热分解性能的研究 12

4。1 绝热加速量热仪工作原理 12

4。2 样品制备及实验方法 SEM储氢材料在硝酸酯类炸药中的应用:http://www.youerw.com/huaxue/lunwen_91065.html