牙科修复用螺环类膨胀单体的合成与表征

时间:2020-11-26 20:49来源:毕业论文
以双酚A双甲基丙烯酸缩水甘油酯(Bis-GMA)为代表的甲基丙烯酸酯类树脂在牙科修复树脂中应用相当广泛,单在聚合过程中普遍存在的体积收缩及应力导致了一系列的临床问题,成为口腔

以双酚A双甲基丙烯酸缩水甘油酯(Bis-GMA)为代表的甲基丙烯酸酯类树脂在牙科修复树脂中应用相当广泛,单在聚合过程中普遍存在的体积收缩及应力导致了一系列的临床问题,成为口腔高分子材料领域亟待解决的问题之一。膨胀单体是一类在聚合过程中能够产生体积膨胀或收缩很小的功能性单体。本研究的主要目的是合成两种螺环原碳酸酯脂类膨胀单体,研究探讨将其应用于对口腔树脂基质甲基丙烯酸酯类单体进行改性以改善其聚合收缩的方法。本文主要是描述了3,9-丙烯氧甲基-3,9-二乙基-1,5,7,11-四氧螺杂[5,5]十一烷(DB-TOSU)和 3,9-二羟甲基-3,9-二乙基-1,5,7,11-四氧螺杂[5,5]十一烷(HB-TOSU)两种膨胀单体的合成及其 1HNMR,FTIR 谱图的表征。使用毛细管法,分组简单测定了两种膨胀单体对牙科树脂聚合收缩的改性效果,并采用最佳三元光引发体系,以不同配比改性牙科常用树脂 Bis-GMA,测定了不同比例混合的 40%膨胀单体改性环氧树脂与Bis-GMA树脂混杂体系的固化收缩率。59970   
毕业论文关键词   牙科修复 聚合收缩 改性 膨胀单体
Title    Synthesis and Characterization of Expanding    Monomers for Dental Restoration                       
Abstract Dental composites are polymeric materials mainly based on methyl methacrylate as resin matrix which is representative of 2,2-bis[4-(2 -hydroxy-3-methacry loxypropl-oxy)phenyl]propane(Bis-GMA). They could be polymerized accompanied by volumetric shrinkage and stress, leading to a serial of clinic failures and became focus of dental  research in polymeric materials.Expanding monomers are a kind of functional compounds with expansion or little shrinkage in the polymerization .The research aimed to synthesize two spiro othorcarbonate expanding monomer and to study the application in modifying the dental resin matrix methacrylate it for the purpose of reducing shrinkage.This article mainly describe Syntheis and Characterization (1HNMR and FTIR)of two Expanding      monomers (3,9-Diethyl-3,9-bis (allyloxymethyl)- 1,5,7,11 –tetraoxaspiro [5,5]) undecane and 3,9-diethyl-3,9- dihydroxymethyl-1,5,7,11- tetraoxaspiro [5,5]undecane and  3,9- diethyl -3,9-dihydroxymethyl- 1,5,7,11- tetraoxaspiro[5,5]undecane).Used capillary method to measure the modification effect of two expanding monomers to the polymerization shrinkage property of dental resin.And used photo initiation system. Modified the commonly used dental resin Bis-GMA in different proportions  and measured the  polymeric shrinkage  of  the mixture of  expanded monomers and Bis-GMA resin hybrid system in different ratio. 
Keywords    Dental Restoration Polymerization Shinkage Expanding Monomer

目次

1引言...1

1.1口腔树脂基质的发展1

1.1.1甲基丙烯酸酯基质系统...1

1.1.2环氧树脂基质系统..2

1.2膨胀单体的发展和研究进展2

1.2.1膨胀单体的发现,分类及特征..2

1.2.2螺环原碳酸酯膨胀单体的合成原理.3

1.2.2膨胀单体的聚合膨胀原理...4

1.3膨胀单体改性树脂的研究及应用...5

1.3.1膨胀单体改性树脂的研究进展..5

1.3.2膨胀单体改性树脂在口腔领域的应用...5

1.4光固化树脂改性的研究6

2实验部分...8

2.1实验原料及仪器...8

2.2单体的合成9

2.2.1DB-TOSU的合成..9

2.2.2HB-TOSU的合成..9

2.3产物的1

H’NMR,FTIR表征...10

2.4单体对牙科树脂的改性测试...11

2.4.1膨胀单体改性环氧树脂与Bis-GMA树脂混杂体系的制备..11

2.4.2单体改性后聚合收缩率的测定.11 牙科修复用螺环类膨胀单体的合成与表征:http://www.youerw.com/huaxue/lunwen_65312.html