丙三醇和CTAB协同作用下草酸铈的形貌控制

摘要：在丙三醇的水溶液环境中，以硝酸铈和草酸为原料，利用超声化学法，在表面活性剂十六烷基三甲基溴化铵（CTAB）的帮助下合成了偏正方形片状堆积的草酸铈金属配合物。对产物用X-射线衍射分析（XRD）、傅里叶红外光谱（FI-IR）、热重分析（TGA）及扫描电子显微镜（SEM）进行了表征，分析讨论了反应时间、CTAB的用量对草酸铈的形貌和大小的影响。以草酸铈为前驱体煅烧得到相应的CeO2，并对CeO2进行X-射线衍射分析（XRD）、可见-紫外光谱（UV）和BET分析等结构表征以及光催化分解性能研究。93552

毕业论文关键词：配位聚合物，草酸铈，二氧化铈，微纳米材料，超声化学法

Abstract: In the mixture solution of glycerol and water, using ultrasonic chemical method, with cerium nitrate and oxalic acid as raw materials, square flake accumulation cerium oxalate was synthesized under the help of the surfactant cetyltrimethyl ammonium bromide (CTAB)。 The products were characterized by powder X- ray diffraction (XRD), Fu Liye infrared spectroscopy (FT-IR), thermal gravimetric (TGA) and scanning electron microscopy (SEM)。 The influence factors of reaction time and the amount of CTAB on hierarchical structure of cerium oxalate were discussed。 Using cerium oxalate as precursor, ceria (CeO2) was obtained through calcination。 For CeO2, its structure was characterized by powder X- ray diffraction (XRD), ultraviolet spec-trum(UV) and specific surface area test (BET)。 Also, photocatalytic activity of CeO2 was inves-tigated。源C于H优J尔W论R文M网WwW.youeRw.com 原文+QQ752-018766

Keywords：coordination polymer , cerium oxalate , ceria , micro/nano-meter material , ultra-sonic chemical method

1 前言 3

2 实验部分 4

2。1仪器 4

2。2试剂 5

2。3草酸铈的制备 5

2。4二氧化铈的制备 5

3 结果与讨论 5

3。1草酸铈的XRD 分析 6

3。2草酸铈的FT-IR 分析 7

3。3草酸铈配合物的热重来自优I尔Q论T文D网WWw.YoueRw.com 加QQ7520~18766 分析 8

3。4草酸铈的SEM分析 9

3。5反应时间对草酸铈结构的影响及形成机理 10

3。6表面活性剂CTAB量对草酸铈结构的影响 13

3。7煅烧偏正方形堆积草酸铈制得样品分析 15

3。7。1二氧化铈的SEM 分析 15

3。7。2二氧化铈的XRD分析 16

3。7。3二氧化铈的BET分析 17

3。7。4二氧化铈的光催化性能 18

3。8前驱体草酸铈及二氧化铈的UV分析 18

4 结论 19

5 参考文献 19

6 致谢 20

1 前言

近年来，纳米材料成为科学家研究的热点。纳米材料是指在三维空间中至少有一维处于纳米尺度范围或由它们作为基本结构单元构成的材料[1]。纳米材料由于其极小的尺度和极高的比表面，会表现出许多块体材料不具有的特殊物理效应，主要包括量子尺寸效应、宏观量子隧道效应、库仑阻塞效应、小尺寸效应、表面效应等，这使得纳米材料有着与常规材料不同的光、电、磁等物理性质,成为二十一世纪科学研究中的重要研究对象[2]。丙三醇和CTAB协同作用下草酸铈的形貌控制:http://www.youerw.com/huaxue/lunwen_201412.html