回收聚碳酸酯(PC)增韧改性的研究

时间:2020-04-17 19:02来源:毕业论文
通过添加PET,使得PET与PC发生反应,引入反应性的官能团羧基(—COOH),可以与扩链剂上面的环氧发生反应,从而达到扩链的作用,起到PC增韧的作用。但核壳结构的增韧剂RC2和RC3的加入

摘要采用一步法,在回收聚碳酸酯中添加PET,引入反应性的官能团羧基(—COOH),然后扩链增韧。本文所用扩链剂为RC1,增韧剂分别为RC2和RC3。通过转矩流变仪,以回收聚碳酸酯(r-PC)与PET,RC1,RC2,RC3,按一定的比例做共混实验,制备共混样品。通过对共混样品做万能材料试验机拉伸实验,断裂面电镜扫描分析,结果表明:通过添加PET,使得PET与PC发生反应,引入反应性的官能团羧基(—COOH),可以与扩链剂上面的环氧发生反应,从而达到扩链的作用,起到PC增韧的作用。但核壳结构的增韧剂RC2和RC3的加入,并没有使得体系的断裂伸张率得到提高,反而下降,而添加RC1和PET的r-PC体系具有较好的强度和断裂伸长率。47798

毕业论文关键词:回收聚碳酸酯;转矩流变仪;混炼;增韧。

Abstract

In this paper, small amount of PET and chain extenders have been added into recycled PC (r-PC) to increase the molecular weight of r-PC. It is expected that the PET can react with PC by transesterification reaction and the reactive –COOH groups were introduced to the r-PC. The following chain extender can reactive with –COOH and the molecular weight of r-PC can be increased.  It was found that RC2 and RC3 do not increase the mechanical performance of r-PC. However, the cooperation of RC1 and PET improves the mechanical properties of r-PC.

Key Words: r-Polycarbonate ; Torque Rheometer; Kneading ; toughening.

目    录

回收聚碳酸酯(PC)增韧改性的研究 1

摘要 2

1.1引言 5

1.2 PC的结构及性能特点 5

1.2.1 力学性能 6

1.2.2 热性能 6

1.2.3 光学性能 7

1.2.4 电性能 7

1.2.5 耐化学试剂和耐腐蚀性能 7

1.2.6 耐老化和燃烧性能 7

1.2.7 相容性 7

1.2.8 流动性 8

1.3  PC的发展现状及应用 8

1.3.1 建筑材料 8

1.3.2 汽车制造 8

1.3.3 医疗器械 8

1.3.4航空航天 8

1.3.5 包装行业 8

1.3.6电器电子 8

1.3.7 光学透镜 9

1.3.8 光盘器材 9

2 实验部分 10

2.1实验原料与试剂 10

2.2实验仪器、设备 10

2.3样本制备 11

2.4万能材料试验机拉伸试验 11

2.5电镜扫描试验(PESEM) 11

3结果与讨论 12

3.1样本拉伸性能 12

3.2样本拉伸性能曲线图 13

3.3增韧剂的使用 16

3.4探索不同的比例的PET和RC1(GP301)的添加量 17

3.5电镜扫描分析(SEM) 18

回收聚碳酸酯(PC)增韧改性的研究:http://www.youerw.com/cailiao/lunwen_50020.html
------分隔线----------------------------
推荐内容