摘要本实验主要是以5mm厚7050铝合金材料为研究对象，对其进行搅拌摩擦焊试验，然后对焊后的接头进行性能检测。内容包括以金相试验观察接头焊缝的显微组织特点，以拉伸试验与硬度试验优化实验工艺参数。87897
试验得出结论，焊核区晶粒均匀细小，热机影响区的组织弯曲变形程度大，呈为条弧状特征，热影响区组织为与母材差别不大的板条状组织，只是稍微有点变形和粗化。 /v在2。67到10之间为最佳工艺参数范围，所得接头抗拉强度良好能达到母材80%左右。另外焊缝上硬度沿水平方向分布为“W”状，且硬度随焊接参数的变化趋势与抗拉强度相似，分析其原因发现与焊接过程中的有效热输入有关。
毕业论文关键词 7050铝合金 搅拌摩擦焊 显微组织 抗拉强度 显微硬度
毕业设计说明书外文摘要
Title Study on friction stir welding process of high strength aluminum alloy
Abstract 7050 aluminum alloy with 5mm thickness friction stir welding is mainly to experiment, and then welded joints start property test。 The contents include through metallographic test to observe the microstructure of the weld joint, through tensile test and hardness test to optimize the experimental process parameters。Results show the grain in weld nugget is tiny size, The thermo- mechanically affected zone organization bending deformation degree, the characteristic is Arc-shaped。 The microstructure of the heat affected zone is a strip structure which is similar to the base material, just a little bit of deformation and coarsening。 the best range of process parameters for /v is between 2。67 to 10。 The tensile strength of the joint can reach about 80% of the base metal。 In addition, the hardness of the weld is distributed as "W" in the horizontal direction。 And the variation tendency of the hardness with the welding parameters is similar to the tensile strength。 Analysis of the reasons, and found that it is related to the effective heat input in the welding process 。
Keywords 7050 aluminum alloy; friction stir welding; microstructure; tensile strength; Micro hardness
目 次
1 绪论 1
1。1 课题背景及意义 1
1。2 铝合金材料的焊接性及特点 1
1。2。1 铝合金材料的焊接性 1
1。2。2 铝合金材料常用焊接方法与特点 2
1。3 搅拌摩擦焊介绍 2
1。3。1 搅拌摩擦焊原理 2
1。3。2 影响搅拌摩擦焊接头性能的主要因素 3
1。3。3 搅拌摩擦焊的应用 3
1。4 铝合金搅拌摩擦焊概况 4
1。4。1 铝合金搅拌摩擦焊国内研究状况 4
1。4。2 铝合金搅拌摩擦焊国外研究状况 6
1。5 本文的研究意义以及主要研究内容 7
2 试验材料及方案设计 8源-于,优Y尔O论U文.网wwW.youeRw.com 原文+QQ75201,8766
2。1 试验材料 8
2。2 试验设备 8
2。2。1 焊机型号及参数 高强铝合金搅拌摩擦焊接工艺研究:http://www.youerw.com/cailiao/lunwen_150169.html