摘要：以草酸和硝酸铈溶液为原料，在表面活性剂聚乙烯吡咯烷酮（PVP）的帮助下，利用磁力搅拌法，合成配位聚合物微纳米草酸铈。对产物进行傅里叶红外光谱（FT-IR）、紫外光谱（UV)、荧光光谱、X-射线衍射（XRD）、扫描电子显微镜（SEM）及热重分析（TGA）表征，研究合成条件如反应时间、PVP量、反应过程所用的不同溶剂等对产物结构的影响。结果表明红外光谱实验结果与晶体结构相符，热重分析显示此配位聚合物经过两个分解过程。以草酸铈为前驱体，在空气气氛中煅烧得到CeO2。79624

毕业论文关键词：磁力搅拌法，微纳米草酸铈，二氧化铈，表征

Abstract: Using magnetic stirring method，coordination polymer micro/nano oxalic acid cerium has been synthesized with oxalic acid solution and cerium nitrate solution as raw material and polyvinylpyrrolidone (PVP) as surface active agent。 Cerium(III) oxalate hydrate has been characterized by Fu Liye infrared spectroscopy (FT-IR), powder X- ray diffraction (XRD), UV spectrum(UV), Fluorescence spectrum, scanning electron microscopy (SEM) and thermal analysis (TGA)。 Systematic investigations have been performed on the factors influencing the product structure, such as reaction time, amount of PVP, different solvents used in the reaction process, etc。 The experimental results show that the infrared spectra are corresponding with the crystal structure and thermogravimetric analysis shows that the coordination polymer occurs two decomposition processes。 By using the Ce(III) oxalate hydrate as precursor, CeO2 has been obtained through calcination in atmosphere。

Keywords: Magnetic stirring method, micro/nano oxalic acid cerium, ceria, characterization

目  录

1 前言 5

2 实验部分 5

2。1 仪器 5

2。2 试剂 5

2。3 草酸铈的制备 5

2。3二氧化铈的制备 6

3 结果与讨论 6

3。1 草酸铈的XRD分析 6

3。2草酸铈的FT-IR分析 6

3。3草酸铈的UV分析 7

3。4 草酸铈的荧光分析 8

3。5草酸铈的TGA分析 9

3。6草酸铈的SEM分析 9

3。6。1反应时间对草酸铈结构的影响 10

3。6。2反应过程所用的不同溶剂对草酸铈结构的影响 11

3。6。3表面活性剂PVP量对草酸铈结构的影响 12

3。7草酸铈的BET分析 13

3。8煅烧片状草酸铈制得样品的分析 14

3。8。1煅烧片状草酸铈制得样品的XRD分析 14

3。8。2煅烧片状草酸铈制得样品的SEM分析 15

结   论 17

参考文献 18

致谢 19

1 前言

铈作为一种重要的稀土元素[1]，在储氢材料、催化领域、光电器件、功能陶瓷、热电材料、燃料电池原料、某些永磁材料、各种合金钢及有色金属等方面都得到了广泛的应用[2]。合成多形态的铈纳米材料，对其进行初步研究有助于理解铈纳米材料的性能、开发及应用。[3]。论文网 片状微纳米草酸铈的可控合成及结构表征:http://www.youerw.com/huaxue/lunwen_92184.html