摘 要：通过磷酸浸泡，辅助微波氧化活化玉米秸秆制备活性炭，用作超级电容器电极材料。采用BET、SEM表征了产物的结构和形貌，结果表明：以18%的磷酸溶液在固液比为1:8条件下浸泡玉米秸秆（4g秸秆，32mL磷酸），浸泡温度80℃，浸泡时间50min，再在功率为700W的微波炉中活化3min条件下制得的活性炭最佳（分三次活化，每次1min），比表面积达1230。37m2/g；采用循环伏安、恒电流充放电和交流阻抗测试方法对其电化学性能进行了研究。循环分析表明，电极在1mol·L–1的H2SO4电解液中，0~1V电位范围内，表现出良好的电容性能，活性炭单体的最大比容量为230。6F·g-1 。79292

毕业论文关键词：  玉米秸秆   活性炭   比容量

Abstract：Soaking in phosphoric acid, and then assisted by microwave oxidation, activated carbon (AC) was successfully synthesized from corn straws, and was used as electrode material of super capacitor。 The obtained active carbon were characterized by BET and SEM technique。 Results show that under the condition of soaking 4g corn straw in 80℃ 32mL 18% phosphoric acid solution for 50min, then activated in 700W microwave for 3min (3 times, each time 1min), the obtained activated carbon possess the optimal BET surface area (1230。37m2/g)。 The electrochemical properties of active carbon were studied by cyclic voltammetry, constant current charge discharge and AC impedance method。 Cycle analysis shows that the obtained optimal activated carbon presented good capacitance performance, and the specific capacity reached 230。6F/g when tested in 1mol/L H2SO4, scanned in the range of 0~1V。 

Key words:  Corn straw, Activated carbon, Specific capacity

目   录

1  绪论 5

2  实验部分 6

2。1  仪器和实验药品 6

2。1。1  实验仪器 6

2。1。2  实验材料 6

2。2  活性炭的制备 6

2。2。1  实验前期准备 6

2。2。2  实验过程记录 6

2。3  活性炭的改进实验 8

2。3。1  实验前期准备 8

2。3。2  改进实验记录 8

2。4  电极材料的制备 11

2。5  电化学测试方法 11

3  结果与讨论 12

3。1  活性炭的表征 12

3。1。1  活性炭的BET表征分析 14

3。1。2  活性炭的电镜分析 14

3。2  活性炭的电化学性能 14

3。2。1  活性炭的循环伏安测试分析 14

3。2。2  活性炭的恒电流充放电测试 17

3。2。3  活性炭的交流阻抗测试分析 18

结论 20

参考文献 21

致谢 22

1  绪论

超级电容器是近年来兴起的一种新型储能装置，它兼具电池和传统电容器的特点，具有比容量大、功率和能量密度高、充电时间短、循环寿命长以及环保低碳的优点，填补了电池和传统电容器之间的空白[1]。作为本世纪重点发展的新型储能产品之一，正在为越来越多的国家和企业争相研制和生产[2]。在电子科技快速发展的今天，新兴的电子产品逐渐主导了我们的生活，超级电容器在电子领域将有极大的发展应用前景。论文网 玉米秸秆制活性炭及其电化学性能优化:http://www.youerw.com/huaxue/lunwen_91593.html