NDA001-HFO 树脂溶出部分Fe(III) 后的吸附性能研究

时间:2020-11-27 11:44来源:毕业论文
当废水中含有络合配体如EDTA时,NDA001-HFO中负载的纳米Fe(III) 氧化物可能被络合溶出,从而导致其吸附性能降低。本文通过NDA001-HFO在Fe(III) 溶出前后对Cu(II)与Ni(II)的静态吸附实验研究溶出

摘要:目前,我国废水中重金属污染问题十分严重。重金属一般不能被分解破坏,只能转移其存在位置和转变其物化形态。树脂基水合氧化铁复合材料(NDA001-HFO)对水中重金属具有很好的吸附去除性能。当废水中含有络合配体如EDTA时,NDA001-HFO中负载的纳米Fe(III) 氧化物可能被络合溶出,从而导致其吸附性能降低。本文通过NDA001-HFO在Fe(III) 溶出前后对Cu(II)与Ni(II)的静态吸附实验研究溶出部分Fe(III) 之后的树脂对重金属的吸附性能影响。60008

毕业论文关键词:水合氧化铁,纳米复合材料,EDTA

Abstract:At present, heavy metal pollution in water is a serious problem in China. Heavy metals are difficult to be deconposed. They can only transfer the location or change its physical form. The HFO-loaded nanocomposite(NDA001-HFO) are proved to show preferable adsorption for heavy metals and to exhibit great potential in disposal of metal-contaminated effluents. The adsorption capability could be apparently decreased in the presence of EDTA through its complexation with and dissolution of Fe(III). According to batch sorption experiment, the sorption capability of NDA001-HFO for heavy metals dropped after Fe(III) dissolution.

Keywords:hydrated ferric oxide, nanocomposite, EDTA

摘要 1

1.  绪论 4

1.1  研究背景 4

1.1.1  重金属废水的来源及危害 4

1.1.2  重金属废水的污染现状 4

1.1.3  重金属废水常规处理技术分析 5

1.1.3.1  化学沉淀法 5

1.1.3.2  电化学法 5

1.1.3.3  膜分离法 5

1.1.3.4  离子交换法 6

1.1.4  纳米水合氧化铁对重金属的深度处理技术 6

1.1.5  重金属废水中EDTA 对纳米水合氧化铁深度处理工艺的影响 8

1.2  本论文研究目标、思路及内容 8

1.2.1  研究目标 8

1.2.2  研究思路 8

1.2.3  研究内容 9

2.1.2  实验方法 10

2.1.2.1  EDTA溶液浸渍 10

2.1.2.2  pH 的影响 10

2.1.2.3  吸附动力学 10

2.1.2.4  竞争离子的影响 11

2.1.3  分析方法 11

2.2.2  吸附动力学分析 13

2.2.3  竞争离子影响分析 15

结 论 16

参考文献 18

致 谢 21

1.  绪论

1.1  研究背景

1.1.1  重金属废水的来源及危害

重金属废水指的是机械制造、仪表、化工、矿冶、电子等工业在生产时排出含有重金属的废水[1],重金属废水的来源十分广泛,最主要来源就是电镀工业废水[2-5]。除了以上来源外,工业废渣、生活垃圾等重金属污染源经过雨水冲刷后,经过地表径流进入水体,也会影响到水中重金属离子的浓度[6-8]。 NDA001-HFO 树脂溶出部分Fe(III) 后的吸附性能研究:http://www.youerw.com/huaxue/lunwen_65354.html