摘要随着人们对环境中微生物的研究和认识不断加深，其作为病原微生物的威胁让人们更加关注。研究一种低浓度且具有高性能的抗菌功能表面将具有重大的实际应用价值。
本文进行了水平氧化锌纳米线表面的制备和银/氧化锌纳米复合表面的抗菌应用研究。通过溶胶凝胶法，旋涂，然后高温烧结制备了负载在玻璃片表面的水平生长的氧化锌纳米线后，用光还原法通过改变光照时间制备了不同载银量的Ag/ZnO纳米线复合表面。最后用扫描电子显微镜（SEM），X射线光电子能谱（XPS），拉曼光谱（Raman）等对材料进行了测试与表征，并探究了不同Ag/ZnO纳米线表面对大肠杆菌的抗菌性能影响。结果表明Ag/ZnO纳米线功能表面就具有较强的抗菌性能。78997
毕业论文关键词 无机抗菌剂 氧化锌纳米线 纳米银/氧化锌 抗菌性能
毕业设计说明书外文摘要
Title The Preparation and Application of an Antibacterial Surface
Abstract With the deepening of the research and understanding of the microorganisms in the environment, it has been drawn more attention in the threat of pathogenic microorganisms。 A functional surface with extremely low level of antibacterial agent and high antibacterial performance is highly desired。
In this paper, horizontal ZnO nanowires were prepared and silver-modified ZnO nanocomposite was studied in details。 Horizontal ZnO nanowires on the normal glass slides were prepared by a simple sol-gel method, followed by spin coating and sintering at high temperatrue。 Ag/ZnO nanowires with different photoreduciton times were prepared。 Ag/ZnO nanowires were characterized by scanning electron microscope, XPS analysis, Raman spectroscopy and so on。 The antibacterial activity for Escherichia coli was investigated by Ag/ZnO with different photoreduction times。The results indicated that Ag/ZnO nanowires on normal glass slides showed excellent antimicrobial properties。
Keywords inorganic antibacterial agent nanowire array silver/zinc oxide nanocomposites antibacterial property
目 次
1 引言 1
1。1 氧化锌纳米功能表面 1
1。1。1 氧化锌纳米线 2
1。2 纳米银的抗菌性能 5
1。2。1 纳米银的发展 5
1。2。2 研究现状 6
1。3 无机抗菌剂的种类与研究 8
1。3。1 银系抗菌剂的抗菌机理 8
1。3。2 ZnO/Ag纳米线复合材料 9
1。4 本课题的研究目的及研究内容 10
2 Ag/ZnO纳米线的制备及表征 11
2。1 实验原料、试剂及分析测试方法 11
2。1。1 实验仪器 11
2。1。2 实验试剂 12
2。1。3 分析测试 12
2。2 实验步骤 13
2。2。1 ZnO纳米线表面的制备 13
2。2。2 Ag/ZnO纳米线表面的制备 银/氧化锌纳米复合表面抗菌制备及其应用:http://www.youerw.com/fanwen/lunwen_91169.html